Tungsten Carbide Resharpening and A good operating practice, combined with well-chosen equipment and a proper care routine can diminish hole deviation and help your operation be as productivity and cost-effective as possible.

Why Button Bit Wear is Important

When a top hammer button bit is sharp, the percussive energy transferred into the rock is at its optimum, resulting in effective rock  fracture and a maximum penetration rate for the given drilling parameters.

As flats develop on the buttons (tungsten carbide inserts), energy utilization is no longer optimized, leading to a lower penetration rate and reduced productivity. As buttons wear, the bit is less effective at fracturing the rock and the energy is dispersed over a larger surface area. Instead, rock is ground, rather than cut, producing smaller cuttings and energy (no longer used for breaking virgin rock) is reflected back up the drill string. This reflective energy contributes to increased loads on the tooling, drifter, and rig. As a general guideline, refurbishing the buttons before the flats reach 1/3 of the button diameter will maintain penetration/productivity, provide maximum bit utilization and help extend the life of all drill string components.

If the button flats are allowed to develop further to where they are considered over-drilled, productivity and the rate of penetration deteriorates. In this situation, much of the rock in contact with the buttons is re-drilled and the steel bit face may make contact with the bottom of the hole. Fewer and smaller rock chips are produced and much of the energy is reflected back up the drill string. This sacrifices the life of all the drill string components is a major contributor to hole deviation, increases wear and tear on drill rig components and results in higher operational costs overall. Top hammer button bits that are over-drilled exhibit broken buttons and impact drilling productivity.

Button bit wear patterns vary depending on the type of ground and the drilling parameters:



Gauge Wear

Harder ground conditions and drilling with excessive rotation creates wear that tends to be greater on the bit circumference.

If drilling through hard materials such as sandstone and quartzite, drilling with excessive rotation, the wear tends to be greater on the bit circumference. Thus, when the buttons are sharpened, the diameter across the gauge is less than or equal to the diameter of the bit body. In this situation, the bit tends to bind (gauge-out) in the hole. Drillers should consider bit replacement or restoring the gauge button-to-body gap to the original (new) condition.

Body Wash

Body wash often occurs when drilling in non-abrasive materials.

When drilling in non-abrasive materials, carbide wear is minimized and drilling intervals are possibly longer. This allows for continued chip removal around the bit and wears away the bit body quicker than the carbides also referred to as body wash. Similar wear occurs in fractured and loose formations where constant hole cleaning and re-drilling of the materials is required for stabilizing the hole and to keep the hole open during retraction. To prevent button loss or shearing under these conditions, the protrusion should be reduced to the original height by scheduling grinding intervals.

Over Drilling

Premature button bit insert failures are substantially reduced when over drilling is eliminated and correct sharpening procedures are performed.

The detrimental effects of over drilling button bits may not be immediately apparent. However, running dull bits not only slows down drilling rates but escalates costs by reducing the life of the drill string components, the rock drill and the rig components. Premature button bit insert failures are substantially reduced when over drilling is eliminated and correct sharpening procedures are performed.